Abstract:
Dye-sensitized solar cells (DSSCs) are emerging as promising candidates to replace expensive silicon
solar cells because of reasonably high efficiency and lower production cost. Photoanodes of these DSSCs
generally have TiO2 particles having the diameters in the range of 15-25 nm, which facilitate the enhanced
dye adsorption due to their large specific surface area. In this research work, mixtures of P25 TiO2 powder
(particle size 22 nm) and P90 TiO2 powder (14 nm) with different weight percentages were used to
prepare the photoanodes for DSSCs. Powder sample mixtures were analyzed by the XRD to identify the
ratio of the anatase and rutile phases present in the above photoanodes. DSSCs fabricated with above
photoanodes were characterized with I-V measurements. Electrical Impedance Spectroscopic
measurements were used to characterize the interfacial resistance of the different interfaces in the DSSC.
The DSSC with the highest power conversion efficiency of 7.0% was fabricated by using a photoanode
fabricated with 70:30 ratios of P25:P90 composite. Factor of 10% efficiency enhancement is achieved by
using this modified photoanode when compared with the conventional P25 photoanode. The best DSSC
showed a short circuit current density of 13.91 mAcm−2, open circuit voltage of 743.9 mV, and a fill factor
of 68%. Observed enhancement in the dye adsorption of the best photoanode would have contributed to
the increment in the photocurrent generation. Therefore, the occupation of the inter-grain spaces in the
P25 matrix by smaller nanoparticles of P90 would have increased the surface area of the photoanode
leading to this efficiency enhancement. Further, this occupation leads to lower the interfacial resistance
between the TiO2 nanocrystallites and the electrolyte from 13.5 to 3.75 . Possible reduction of trap
states due to this occupation would also have contributed to this efficiency enhancement by lowering the
electron recombination dynamics of DSSC.