Abstract:
WS2 (Transition-metal dichalcogenide) are known for their novel electro catalytic properties and
have analogous structure with graphene. It is noted that catalytic performance of WS2 can be further
increased by doping either heteroatom or transition metal. Facile one-pot hydrothermal method was used
for synthesis of WS2 quantum dots and WS2 nanorods, Nanocubes are prepared by simple chemical ageing
method. The obtained WS2 quantum dots, WS2 nanorods show good transmittance in visible region
(400 – 800 nm). The photoluminescence peak was obtained around 420 nm for WS2 quantum dots, CoFe
shows high intense peak at around 424 nm confirms the product quality. Raman active modes of CoFe
around 501 cm-1 (T1g) and 620 cm-1 (A1g) reveals cubic structure formation. The structural features of the
as prepared (0D/3D), (1D/3D) are characterized systematically by the X-ray diffraction, Field emission
scanning electron microscopy, EDAX, High-resolution transmission electron microscopy, FTIR and Raman
spectroscopy. Here we identified the synergistic effect of the prepared hybrid WS2 quantum dots/Co-Fe
nanocubes (0D/3D), WS2 nanorods/ Co-Fe nanocubes (1D/3D) by appropriate doping composition shows
more exposed edge sites, large specific surface area and outstanding catalytic activities, when compared
with bare WS2 and CoFe and it is a real substitute for Pt-counter electrode in Dye sensitized solar cells.