Abstract:
One of the common hindrance to the higher power conversion efficiencies in any kind of solar cells
is the charge recombination. In the case of dye-sensitized solar cells, porous electrode (typically TiO2 or
other wide bandgap semiconducting oxides) / dye interface is a hot recombination centre, where the
electrons recombine either with the oxidized dye or the electrolyte. The above-said process inhibits the
power conversion efficiency as it decreases the photo-generated current and the open circuit potential of
the cell. Generally, to overcome this, wide band gap insulating oxide coating of few nanometre thicknesses
is employed. Some of the important parameters for the choice of the coating material includes the Position
of bands, the oxidation state, and the structural modifications in the TiO2 layer induced by coating. In this
work, hydrogenated carbon (a-C:H) layer were coated over the TiO2 thin films by Plasma assisted chemical
vapour deposition technique. Acetylene and argon mixture was used as precursor. Hydrogenated carbon
coated TiO2 were analysed using X-ray diffraction analysis, and the sample showed characteristic anatase
phase of TiO2, peaks corresponding to the carbon coating were not observed owing to its insulating nature.
Optical properties were studied using UV-visible absorption analysis, and it showed strong absorption in
the UV region. TEM analysis was done by scratching out the coating from the films, and it reveals a thin
amorphous carbon layer deposited over the TiO2 nanoparticles. XPS analysis revealed the chemical states
of the prepared material. Further, Mott-Schottky Measurements were carried out for the coated TiO2 layer
to study the flat band potential of the material. The dye-sensitized solar cells were constructed using the
prepared material and its power conversion efficiencies were studied. Further, to study the charge
recombination, transport properties and electron life time of the cells, electrochemical impedance
measurements were carried out.